热塑性弹性体

普立万公司

Technical Data

产品说明

Versaflex™ FFC 2882-70

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  普立万公司

• Versaflex™

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

特性 • 食品接触的合规性

用途 • 包覆成型 • 垫圈 • 容器

• 厨具 • 非特定食品应用 • 消费品应用领域

机构评级 • FDA 21 CFR 177.2600 2 • NSF 51 3 • 欧洲 10/1/2011 12:00:00 AM 4

RoHS 合规性 • RoHS 合规

外观 • 半透明 • 黑色

形式 • 粒子

加工方法 • 挤出 • 注射成型

物理性能 额定值(英制) 额定值(公制) 测试方法

密度 / 比重 0.880 0.878g/cm³ ASTM D792

弹性体 额定值(英制) 额定值(公制) 测试方法

拉伸应力 6, 7 (300%应变, 73°F (23°C)) 428psi 2.95MPa ASTM D412

抗张强度 6, 7 (断裂, 73°F (23°C)) 900psi 6.21MPa ASTM D412

伸长率 ASTM D412

断裂 1200% 1200%

断裂, 73°F (23°C) 6, 7 1200% 1200%

硬度 额定值(英制) 额定值(公制) 测试方法

肖氏硬度 (邵氏 A, 10 秒) 73 73 ASTM D2240

充模分析 额定值(英制) 额定值(公制) 测试方法

表观粘度 (392°F (200°C), 11200 sec^-1) 38.6Pa•s 38.6Pa•s ASTM D3835

注射 额定值(英制) 额定值(公制)

建议的最大回制料比例 20% 20%

料筒后部温度 380 到 400°F 193 到 204°C

料筒中部温度 390 到 420°F 199 到 216°C

料筒前部温度 400 到 440°F 204 到 227°C

射嘴温度 410 到 460°F 210 到 238°C

加工（熔体）温度 400 到 440°F 204 到 227°C

模具温度 55 到 90°F 13 到 32°C

背压 0.00 到 80.0psi 0.00 到 0.552MPa

螺杆转速 50 到 100rpm 50 到 100rpm

 

 

Versaflex™ FFC 2882-70

热塑性弹性体

普立万公司

 

注射说明

Color concentrates based on polypropylene (PP), ethylene vinyl acetate (EVA), or low density polyethylene (LDPE) are most suitable for coloring Versaflex™ FFC 2882-70. Improved color dispersion can be achieved by using higher melt flow concentrates (with a melt flow from 25-40 g/10 min). Typical loadings for color concentrates are 1% to 5% by weight. Liquid color can be used, but mineral oil based carriers may have a significant effect on the final hardness value. Concentrates based on PVC should not be used. A high color match consistency can be obtained by the use of precolored compounds available from GLS. The final determination of color concentrate suitability should be determined by customer trials.

 

Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).

 

Regrind levels up to 20% can be used with Versaflex™ FFC 2882-70 with minimal property loss, provided that the regrind is free of contamination. To minimize losses during molding, the melt temperature should remain as low as possible. The final determination of regrind effectiveness should be determined by the customer.

 

Versaflex™ FFC 2882-70 has excellent melt stability. Maximum residence times may vary, depending on the size of the barrel. Generally, the barrel should be emptied if it is idle for periods of 8 - 10 minutes or longer.

 

Drying is not Required

Injection Speed: 1 to 3 in/sec

1st Stage - Boost Pressure: 500 to 700 psi

2nd Stage - Hold Pressure: 10 to 30% of Boost

Hold Time (Thick Part): 2 to 4 sec

Hold Time (Thin Part): 1 to 2 sec

挤出 额定值(英制) 额定值(公制)

熔体温度 400 到 440°F 204 到 227°C

口模温度 420 到 460°F 216 到 238°C

挤压说明

Rear: 380-400F

Center: 390-420F

Front: 400-440F

Screw: 100-500rpm

 

 

 

 