NSF饮用水处理PA66，玻璃纤维增强材料50%，泵件，阀门/阀门部件，饮用水接触许可，FDA食品接触的合规性

 

TECHNYL® A 218W V50 BLACK FA

聚酰胺 66

Solvay Engineering Plastics

Technical Data

 

产品说明

TECHNYL® A 218W V50 Black FA is a polyamide 66, reinforced with 50% of glass fibre, heat stabilized, for injection moulding, with improved hydrolysis resistance. This grade offers an improved hydrolisis resistance, as well as an excellent combination between thermal and mechanical properties. It also restricts electrolytical corrosion. It is designed to be used in food contact and drinking water applications.

总览

材料状态 • 已商用：当前有效

资料 1 • Technical Datasheet

搜索 UL 黄卡 •  Solvay Engineering Plastics

•  TECHNYL®

供货地区 • 北美洲 • 拉丁美洲 • 亚太地区

• 非洲和中东 • 欧洲

填料/增强材料 • 玻璃纤维增强材料, 50% 填料按重量

添加剂 • 热稳定剂

特性 • 尺寸稳定性良好 • 食品接触的合规性 • 饮用水接触许可

• 高刚性 • 脱模性能良好

用途 • 泵件 • 阀门/阀门部件 • 消费品应用领域

• 大型家用电器和小型家用电器 • 工业应用

• ACS 未评级 • EC 1907/2006 (REACH) • WRAS 未评级

机构评级 • ANSI Unspecified Rating • KTW 未评级

• DVGW Unspecified Rating • NSF 未评级

RoHS 合规性 • RoHS 合规

外观 • 黑色

形式 • 粒子

加工方法 • 注射成型

树脂 ID (ISO 1043) • PA66-GF50

物理性能 干燥 调节后的 单位制 测试方法

密度 1.55 -- g/cm³ ISO 1183/A

收缩率 ISO 294-4

垂直 0.75 -- %

流动 0.14 -- %

吸水率 (24 hr, 23°C) 0.60 -- % ISO 62

机械性能 干燥 调节后的 单位制 测试方法

拉伸模量 (23°C) 16300 12500 MPa ISO 527-2/1A

拉伸应力 (断裂, 23°C) 230 175 MPa ISO 527-2/1A

拉伸应变 (断裂, 23°C) 2.0 2.5 % ISO 527-2

弯曲模量 (23°C) 13500 10000 MPa ISO 178

冲击性能 干燥 调节后的 单位制 测试方法

简支梁缺口冲击强度 (23°C) 14 18 kJ/m² ISO 179/1eA

简支梁无缺口冲击强度 (23°C) 88 85 kJ/m² ISO 179/1eU

悬壁梁缺口冲击强度 (23°C) 14 16 kJ/m² ISO 180

热性能 干燥 调节后的 单位制 测试方法

热变形温度 (1.8 MPa, 未退火) 255 -- °C ISO 75-2/Af

熔融温度 263 -- °C ISO 11357-3

电气性能 干燥 调节后的 单位制 测试方法

表面电阻率

-- 6.0E+13 1.0E+11 ohms ASTM D257

-- 1.0E+14 1.0E+12 ohms IEC 60093

介电强度 (2.00 mm) 35 30 kV/mm IEC 60243-1

相对电容率 3.70 4.00 IEC 60250

耗散因数 0.010 0.11 IEC 60250

漏电起痕指数 (解决方案 A) 400 -- V IEC 60112

 

TECHNYL® A 218W V50 BLACK FA

聚酰胺 66

Solvay Engineering Plastics

可燃性 干燥 调节后的 单位制 测试方法

UL 阻燃等级 UL 94

0.8 mm HB --

1.6 mm HB --

3.2 mm HB --

灼热丝易燃指数 IEC 60695-2-12

0.8 mm 650 -- °C

1.6 mm 650 -- °C

3.2 mm 700 -- °C

极限氧指数 23 -- % ISO 4589-2

注射 干燥单位制

干燥温度 80°C

建议的最大水分含量 0.20%

料筒后部温度 270 到 280°C

料筒中部温度 280 到 290°C

料筒前部温度 280 到 300°C

模具温度 70 到 100°C

注射说明

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4h

 

Injection Advice:

 

• For reinforced polyamides, Solvay recommends the use of steel with a high content of carbon, and purified for polishing, to avoid or limit the abrasion. For example: X38CrMoV5-1 (EN Norm) - 1.2367 /1.2343 (DIN Norm) or X160CrMoV12 (EN Norm) - 1.2601 /1.2379 (DIN Norm). In the case of high requirements on surface quality a mould temperature of up to 120°C can be considered. 

 

• The processing parameters like processing temperatures are a recommendation and can be adjusted in function of injection machine size, part geometry / design 

 

 

 

NSF饮用水处理PA66聚酰胺66,NSF饮用水处理PA66,PA66 TECHNYL® A 218W V50 BLACK FA塑料是东莞市双帮塑胶原料有限公司常年销售的塑料，因为塑料价格行情每天都有新变化前天的报价不等于今天的报价。本公司销售的所有原料保证是原厂原包,随料可以提供生产厂商提供的物性表、SGS报告，ROHS报告，REACH报告  SVHC报告，COA出厂报告,提供原料注塑加工工程中可能出现的各种异常现象解决方法，塑料牌号太多，本网站没有提供的本公司也有代理，详情请咨询本公司相关业务人员0769-87795123  微信：13549213581     联系电话：13549213581肖生  

 

 