UBESTA P3012 U    
    
聚酰胺12    
    
UBE Engineering Plastics, S.A.   
     
 Technical Data    
     

产品说明

UBESTA P3012 U is a low viscosity, a heat stabilized, natural PA12 powder with a high MFR-value. It is suitable for application which demand a powder good flow-ability of the polymer. UBESTA 3012 U offers good viscosity stability in compounding of highly filled systems as used for plastics magnets. UBESTA 3012 U shows only low moisture absorption and therefore exceptional dimension stability.

总体

材料状态 • 已商用：当前有效   
 •  Technical Datasheet (English)
  
资料 1 •  Processing - Injection Molding (English)
 
 •  Processing - Extrusion (English)
 
Search for UL Yellow Card •  UBE Engineering Plastics, S.A.
  
供货地区 • 欧洲   
添加剂 • 热稳定剂   
性能特点 • 尺寸稳定性良好 • 流动性高 • 吸潮性差 
 • 低粘度 • 热稳定性  
    
外观 • 自然色   
形式 • 粉状   
加工方法 • 注射成型   

 物理性能 额定值单位制 测试方法
 密度 1.02g/cm³ ISO 1183
 熔流率 (190°C/1.0 kg) 17g/10 min ISO 1133
 收缩率  ISO 294-4
 横向流量 0.90% 
 流量 0.80% 
 吸水率 (23°C, 24 hr) 0.60% ISO 62
 机械性能 额定值单位制 测试方法
 拉伸应力 (屈服) 47.0MPa ISO 527-2
 拉伸应变  ISO 527-2
 屈服 5.0% 
 断裂 200% 
 弯曲模量 1500MPa ISO 178
 弯曲强度 62.0MPa ISO 178
 冲击性能 额定值单位制 测试方法
 简支梁缺口冲击强度  ISO 179/1eA
 -40°C, 完全断裂 3.0kJ/m² 
 23°C, 完全断裂 3.0kJ/m² 
 硬度 额定值单位制 测试方法
 洛氏硬度 (R 计秤) 105 ISO 2039-2
 支撐硬度 (邵氏 D) 77 ISO 868
 热性能 额定值单位制 测试方法
 热变形温度  
 0.45 MPa, 未退火 103°C ISO 75-2/B
 1.8 MPa, 未退火 48.0°C ISO 75-2/A
 溶融温度（DSC） 180°C ISO 3146
 线形膨胀系数 - 流动 0.00015cm/cm/°C ISO 11359-2
 电气性能 额定值单位制 测试方法
 体积电阻率 1.0E+15ohm•cm IEC 60093
 补充信息  
 The value listed as Melting Temperature, ISO 3146, was tested in accordance with ISO 11357. 
 Tensile Strain at Break, ISO 527: >200%  
 Abrasion Loss, ISO 9352, CS-17, 1000 rev.: 6 mg  
1 / 3  
 
UBESTA P3012 U
聚酰胺12
UBE Engineering Plastics, S.A. 

备注
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。

2 一般属性：这些不能被视为规格。