VESTAMID® LX9057 orange E20081
聚酰胺12

Evonik Degussa GmbH  
    
 Technical Data   
    

产品说明

Low viscosity, self-extinguishing polyamide 12 compound, free of halogen

VESTAMID LX9057 orange E20081 is a heatstabilized compound with an efficient halogen-free flame retardant. Tested according to UL94, it complies with the flammability classification V-0.

The halogen-free formulation makes VESTAMID LX9057 orange E20081 especially suitable for the electronic and cable industry.

VESTAMID LX9057 orange E20081 can be used for injection molding as well as for wire extrusion coating. The semi-crystalline compounds based on PA 12 only absorb small amounts of water. Therefore manufactured parts exhibit excellent dimensional stability at changing ambient humidity, constant high toughness, low coefficient of friction and good chemical resistance.

Due to the presence of flame retardant melt temperature should not exceed 240 °C. We recommend melt temperatures of 200 °C- 220 °C.

总体

 材料状态 • 已商用：当前有效   
 资料 1 •  Technical Datasheet (English)
  
 Search for UL Yellow Card •  VESTAMID®
  
 供货地区 • 北美洲 • 欧洲  
 添加剂 • 热稳定剂 • 阻燃  
   • 半结晶 • 耐化学性良好 • 吸潮性差 
 性能特点 • 尺寸稳定性良好 • 热稳定性  
  • 低摩擦系数 • 韧性良好 • 阻燃性能 
      
   • 低粘度 • 无卤  
 用途 • 电缆护套 • 电气/电子应用领域 • 电线电缆应用 
 外观 • 橙色   
 形式 • 颗粒   
 加工方法 • 挤压层涂法 • 金属线挤出 • 注射成型 
     
 物理性能  额定值单位制 测试方法 
 密度  1.05g/cm³ ISO 1183 
 机械性能  额定值单位制 测试方法 
 拉伸模量  1100MPa ISO 527-2 
 拉伸应力 (屈服)  37.0MPa ISO 527-2 
 拉伸应变   ISO 527-2 
  屈服  13%  
  断裂  > 100%  
 冲击性能  额定值单位制 测试方法 
 简支梁缺口冲击强度 (23°C, 完全断裂)  5.0kJ/m² ISO 179/1eA 
 简支梁缺口冲击强度 (23°C)  无断裂 ISO 179/1eU 
 热性能  额定值单位制 测试方法 
 熔融温度 3  176°C ISO 11357-3 
 可燃性  额定值单位制 测试方法 
 UL 阻燃等级 (0.800 mm)  V-0 UL 94 
     
 注射  额定值单位制  
 加工（熔体）温度  200 到 220°C  
 挤出  额定值单位制  
 熔体温度  200 到 220°C  
 备注    
1 通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。  
 2 一般属性：这些不能被视为规格。    
 3 2nd Heating    
1 / 2