Trilliant™ HC HC6200-5001 XR Grey
聚酰胺12
普立万公司 

Technical Data

产品说明

The Trilliant® specialty compounds offer a complete system of specialty engineered materials, certified processes, services and technical support that enable healthcare OEM's to get to market ahead of competition. When specified, Trilliant® compound may incorporate agency rated materials that meet USP Class IV, FDA or ISO 10993 testing requirements.

This Trilliant® grade is a high density specialty compound featuring a sustainable material solution for radiation shielding and weighting & balancing applications. The composite material offers a high performance thermoplastic-based alternative to lead. This compound has densities similar to traditional metals and provides greater flexibility in design and processing.

总体

 材料状态 • 已商用：当前有效   
 资料 1 •  Technical Datasheet
  
 Search for UL Yellow Card • 普立万公司   
 供货地区 • 北美洲 • 南美洲 • 亚太地区 
  • 非洲和中东 • 欧洲  
      
 性能特点 • 高比重 • 无毒性  
 用途 • 砝码和天平 • 型号  
  • 辐射屏蔽 • 医疗/护理领域的应用  
      
 外观 • 灰色   
 形式 • 颗粒料   
 加工方法 • 注射成型   
      
 物理性能   额定值单位制 测试方法 
 密度   11.0g/cm³ ISO 1183 
 收缩率   0.40 到 0.80% ISO 294-4 
 机械性能   额定值单位制 测试方法 
 拉伸模量   8000MPa ISO 527-2/1 
 拉伸应力 (断裂)   45.0MPa ISO 527-2/50 
 拉伸应变 (断裂)   0.50 到 1.0% ISO 527-2/50 
 弯曲模量   10000MPa ISO 178 
 弯曲强度   75.0MPa ISO 178 
 冲击性能   额定值单位制 测试方法 
 简支梁缺口冲击强度   5.0kJ/m² ISO 179 
 简支梁缺口冲击强度   10kJ/m² ISO 179 
 热性能   额定值单位制 测试方法 
 热变形温度     
 0.45 MPa, 未退火   160°C ISO 75-2/B 
 1.8 MPa, 未退火   130°C ISO 75-2/A 
 导热系数 3   3.0 到 3.5W/m/K ASTM E1461 
 电气性能   额定值单位制 测试方法 
 表面电阻率   < 1.0E+3ohm IEC 60093 
 补充信息     
 Shielding properties:     
 Attenuation coefficient at 511 keV = 0.94cm-1   
 Half Thickness at 511 keV = 0.74cm     
      
 注射   额定值单位制  
 干燥温度   80.0°C  
 干燥时间   4.0hr  
 加工（熔体）温度   230 到 280°C  
 模具温度   65.0 到 100°C  